AG SRP or Zymol HD Cleanes

A

aRYip

New member
After review the two thread



http://www.autopia.org/forum/guide-detailing/77859-test-swirl-removal-hand.html

http://www.autopia.org/forum/car-de...713-review-glaze-really-does-hide-swirls.html



I narrow down my choice to either Autoglym SRP or Zymol HD Cleanes



I heard that Autoglym SRP can not remove any swirl, but hide, so does Zymol HD Cleanes?

If both are hide only, what about opt poli-seal? is it better?



Which one is better one if I do it by hand.



By the way:

Clay --> Wash --> SRP or HD --> Wash --> Wax (This is the correct way right?)

And is Opti-seal before wax necessary?



Sorry for lot of newbi questions... :hide:
 
I just got SRP for Father's Day and have only had time to try it on a couple panels, but IMO it is much easier than Poli-Seal to apply by hand. Removal is about the same. I do like Poli-Seal by machine, but not by hand.
 
Thanks for the reply,

um, then I think i will get the AG SRP since there lot of good reviews

Do you think I should apply Scratch x first after Clay Bar, then follow by SRP then wax due to the SRP is just the filler, and Scratch X is not.
 
aRYip said:
..I think i will get the AG SRP since there lot of good reviews

Do you think I should apply Scratch x first after Clay Bar, then follow by SRP then wax due to the SRP is just the filler, and Scratch X is not.
Click to expand...



Good plan. Remove/lessen what you can with the Scratch-X and then use SRP topped with wax.



Might want to try Ultimate Compound instead of the Scratch-X.



Don't wash between the SRP and the wax, it might wash away some of the stuff the SRP leaves behind.
 
Accumulator said:
Good plan. Remove/lessen what you can with the Scratch-X and then use SRP topped with wax.



Might want to try Ultimate Compound instead of the Scratch-X.



Don't wash between the SRP and the wax, it might wash away some of the stuff the SRP leaves behind.
Click to expand...





does the ultimate compound or scratch x 2.0 have more cut?
 
I heard UC has more cutting power than the Scratch X, and SRP has no or very litter cut since it filler

By the way, I think I would go with OPT Poli-Seal since its one step product, clean, polish and sealant, and have both filler and cut in it.
 
335i said:
does the ultimate compound or scratch x 2.0 have more cut?
Click to expand...



As aRYip noted, the UC has much more cut. Some people say UC finshes out OK but I'd plan to follow up with a quick polish using the Scratch-X. But the SRP will probably conceal any micromarring from the UC and make things look OK, just not as nice as they *could* look.
 
You must log in or register to reply here.